PERILAKU LEACHING DARI ROASTED LATERITE ORE DALAM PENINGKATAN REKOVERI LOGAM

Gyan Prameswara

doi:10.61844/jtkm.v2i2.500

Penulis

Gyan Prameswara Program Studi Teknik Kimia Mineral, Politeknik ATI Makassar https://orcid.org/0000-0001-8966-3393

DOI:

https://doi.org/10.61844/jtkm.v2i2.500

Kata Kunci:

Roasting, Laterit, Karakteristik mineral, Geotit, Dehidroksilasi

Abstrak

Tujuan dari penelitian ini adalah untuk mengkaji pengaruh roasting terhadap karakteristik mineral bijih laterit. Roasting dilakukan dengan menggunakan muffle furnace pada temperatur 280 °C dan 610 °C selama 3 jam. Raw material dan sampel hasil roasting kemudian di karakterisasi dengan menggunakan x-ray fluorescence dan spektrometri x-ray diffraction. Analisis x-ray diffraction mengkonfirmasi keberadaan lizardite, geotit, dan hematite dalam raw ore. Selain itu, perubahan fasa yang menarik diamati selama proses roasting, dengan geotit yang berubah menjadi hematit pada suhu 280 °C dan lizardite yang berubah menjadi enstatite menjadi forsterite pada suhu 610 °C. Selain itu, konsentrasi logam menunjukkan peningkatan secara keseluruhan dengan meningkatnya suhu pemanggangan, kecuali untuk Zn. Hasil penelitian ini memiliki implikasi yang signifikan terhadap pengolahan bijih laterit. Khususnya, proses roasting dapat meningkatkan kemampuan leaching laterit, yang berpotensi memudahkan proses ekstraksi dan pemurnian selanjutnya. Hasil penelitian ini memberikan kontribusi terhadap pemahaman yang lebih mendalam tentang perubahan mineralogi yang disebabkan oleh roasting, sehingga memberikan informasi yang berharga untuk optimalisasi teknik pengolahan bijih laterit.

Unduhan

Data unduhan belum tersedia.

Referensi

U. König, “Nickel laterites—mineralogical monitoring for grade definition and process optimization,” Minerals, vol. 11, no. 11, 2021, doi: 10.3390/min11111178.

S. Kursunoglu and M. Kaya, “Hydrometallurgical Processing of Nickel Laterites- a Brief Overview on the Use of Solvent Extraction and Nickel/Cobalt Project for the Separation and Purification of Nickel and Cobalt,” Bilimsel Madencilik Dergisi, vol. 58, no. 2, pp. 131–144, 2019, doi: 10.30797/madencilik.580147.

I. A. Goonetilleke, H. C. S. Subasinghe, A. S. Ratnayake, and D. T. Jayawardana, “Acid-assisted leaching of iron and manganese from sri lankan laterite: A potential source of alumina production,” J Natl Sci Found, vol. 49, no. 2, pp. 303–310, 2021, doi: 10.4038/jnsfsr.v49i2.10177.

L. Panda, D. S. Rao, B. K. Mishra, and B. Das, “Characterization and dissolution of low-grade ferruginous nickel lateritic ore by sulfuric acid,” Min Metall Explor, vol. 31, no. 1, pp. 57–65, Feb. 2014, doi: 10.1007/BF03402349.

W. Astuti, T. Hirajima, K. Sasaki, and N. Okibe, “Kinetics of nickel extraction from Indonesian saprolitic ore by citric acid leaching under atmospheric pressure,” Min Metall Explor, vol. 32, no. 3, pp. 176–185, Aug. 2015, doi: 10.1007/BF03402286.

J. Li, D. Xiong, H. Chen, R. Wang, and Y. Liang, “Physicochemical factors affecting leaching of laterite ore in hydrochloric acid,” Hydrometallurgy, vol. 129–130, pp. 14–18, 2012, doi: 10.1016/j.hydromet.2012.08.001.

W. Xiao, X. Liu, and Z. Zhao, “Kinetics of nickel leaching from low-nickel matte in sulfuric acid solution under atmospheric pressure,” Hydrometallurgy, vol. 194, no. April, p. 105353, 2020, doi: 10.1016/j.hydromet.2020.105353.

J. Li, X. Li, Q. Hu, Z. Wang, Y. Zhou, J. Zheng, W. Liu, and L. Li, “Effect of pre-roasting on leaching of laterite,” Hydrometallurgy, vol. 99, no. 1–2, pp. 84–88, 2009, doi: 10.1016/j.hydromet.2009.07.006.

W. Dahani, I. G. N. B. S. Jaksa, I. Marwanza, R. Kurniawati, and S. Subandrio, “The effect of pre-roasting on nickel extraction from limonite ore by acid leaching method,” AIP Conf Proc, vol. 2267, no. September, 2020, doi: 10.1063/5.0015935.

P. P. M. Ribeiro, I. D. dos Santos, R. Neumann, A. Fernandes, and A. J. B. Dutra, “Roasting and Leaching Behavior of Nickel Laterite Ore,” Metallurgical and Materials Transactions B: Process Metallurgy and Materials Processing Science, vol. 52, no. 3, pp. 1739–1754, 2021, doi: 10.1007/s11663-021-02141-6.

K. C. Wanta, F. H. Tanujaya, R. F. Susanti, H. T. B. M. Petrus, I. Perdana, and W. Astuti, “Studi Kinetika Proses Atmospheric Pressure Acid Leaching Bijih Laterit Limonit Menggunakan Larutan Asam Nitrat Konsentrasi Rendah,” Jurnal Rekayasa Proses, vol. 12, no. 2, p. 19, Dec. 2018, doi: 10.22146/jrekpros.35644.

G. Prameswara, F. Y. P. Tyassena, I. Amin, and H. Hatimah, “OPTIMIZATION OF LATERITE ORE GRINDING PROCESS USING BALL MILL WITH RESPONSE SURFACE METHOD,” Metalurgi, vol. 37, no. 3, pp. 119–126, 2022.

H. Hatimah, I. Amin, F. Y. P. Tyassena, and G. Prameswara, “Pengaruh Kominusi Dengan Menggunakan Ball Mill Terhadap Karakteristik Ore Nikel Dari Morowali,” Jurnal Teknologi Kimia Mineral, vol. 1, no. 1, pp. 10–13, 2022.

G. Prameswara, F. Y. P. Tyassena, M. Pasaribu, and I. N. Febryanzha, “Kinetika Leaching Ni dan Fe dari Bijih Laterit Tipe Limonite Morowali,” REACTOR: Journal of Research on Chemistry and Engineering, vol. 3, no. 2, pp. 57–62, 2022.

G. Prameswara, F. Y. P. Tyassena, M. Pasaribu, I. Trisnawati, and H. T. B. M. Petrus, “Nickel Recovery Optimization and Kinetic Study of Morowali Laterite Ore,” Transactions of the Indian Institute of Metals, vol. 76, no. 5, pp. 1341–1348, May 2023, doi: 10.1007/s12666-022-02858-1.

I. Setiawan, “Karakteristik Nikel Laterit Indonesia pada Pemanasan dari 600 C sampai dengan 1000 C,” in Seminar Nasional Sains dan Teknologi 2016, 2016, no. November, pp. 58–66.