Pengaruh Perlakuan Panas terhadap Kekerasan dan Kekasaran Permukaan Hasil Pembubutan Baja AISI 1045
DOI:
https://doi.org/10.61844/jemmtec.v4i02.943Keywords:
AISI 1045, Perlakuan panas, Kekasaran permukaan, Kekuatan tarikAbstract
This study examines the effects of heat treatment on the hardness, tensile strength, and surface roughness of AISI 1045 steel during turning operations. The material was tested under three conditions: untreated, hardened (with water and oil quenching), and tempered. Results reveal that heat treatment transformed the microstructure from ferrite-pearlite to a combination of martensite, bainite, ferrite, and pearlite. Hardness increased from 52.83 HRC (untreated) to 80.17 HRC (water-quenching hardening) and 68.33 HRC (oil-quenching hardening). Tempering achieved the highest tensile strength at 1231.73 MPa with a hardness of 65 HRC. Surface roughness was lowest for tempered specimens at 700 RPM (3.6 µm), while water-quenching hardening at 1000 RPM resulted in the highest roughness (35.35 µm). Tempering is recommended for machine components such as shafts due to its optimal balance of mechanical properties, hardness, and surface quality.
References
Singh, S., Samir, S., Kumar, K., & Thapa, S. (2021). Effect of heat treatment processes on the mechanical properties of AISI 1045 steel. Materials Today: Proceedings, 45, 5097-5101.
Rifnaldy, R., & Mulianti, M. (2019). Pengaruh Perlakuan Panas Hardening Dan Tempering Terhadap Kekerasan (Hardness) Baja AISI 1045. Ranah Research: Journal of Multidisciplinary Research and Development, 1(4), 950-959.
Akhyar, I., & Sayuti, M. (2015). Effect of heat treatment on hardness and microstructures of AISI 1045. Advanced Materials Research, 1119, 575-579.
Kuntoğlu, M., & Sağlam, H. (2019). Investigation of progressive tool wear for determining of optimized machining parameters in turning. Measurement, 140, 427-436.
Veiga, F., Arizmendi, M., Jiménez, A., & Del Val, A. G. (2021). Analytical thermal model of orthogonal cutting process for predicting the temperature of the cutting tool with temperature-dependent thermal conductivity. International Journal of Mechanical Sciences, 204, 106524.
Farhat, Z. N. (2003). Wear Mechanism of CBN Cutting Tool During High-Speed Machining of Mold Steel. Materials Science and Engineering: A, 361(1-2), 100-110.
Muthu Krishnan, G., & Pradeep Kumar, J. (2022). Machinability and Surface Integrity Characteristics in Hard Turning of High Hardened Steels Using Different Types of Inserts. In Materials, Design and Manufacturing for Sustainable Environment: Select Proceedings of ICMDMSE 2022 (pp. 257-270). Singapore: Springer Nature Singapore.
Kim, B. J., Jung, S. S., Hwang, J. H., Park, Y. H., & Lee, Y. C. (2019). Effect of eutectic Mg2si phase modification on the mechanical properties of Al-8Zn-6Si-4Mg-2Cu cast alloy. Metals, 9(1), 32.
Sekeroney, C., Nanulaita, N. J. ., Dematacco, F. ., Fikri, M. A. ., & Febriana, I. D. . (2023). Pengaruh Temperature Tempering Terhadap Kekerasan Pada Baja Karbon Sedang Hasil Pengelasan FCAW (Flux-Cored Arc Welding). Journal Mechanical Engineering, 1(3), 169–172. https://doi.org/10.31959/jme.v1i3.2098
Supriadi, H., Primartin, A., Zulhanif, Z., & Suudi, A. (2024). Pengaruh Temperatur Tempering Terhadap Energi Impak Dan Pola Patahan Pada Baja AISI 1045. Turbo: Jurnal Program Studi Teknik Mesin, 13(1).